SafeEndo ReCreate LC

Universal Nano Hybrid Restorative Composite

Features

Brand : SafeEndo
SafeEndo ReCreate LC : SafeEndo ReCreate LC

SafeEndo ReCreate LC - 1 Unit

636.00

Shipping : Free Shipping | See details
Item Location: Jalandhar, India
Delivery: Estimated between Thursday 4th of June - Monday 8th of June
Payments:
Returns: 10 day returns. Seller pays for return shipping | See details

The Dentist Shop Assurance

Manufacturer Warranty
100% Genuine Products
Secure Payment
Brand New

Description

DESCRIPTION:

Universal restorative material ReCreateLC is a nano-hybrid radiopaque light-cured composite which can be easily shaped, does not stick to the instrument, cured under 400-500 nm wavelengths light and polished to a "dry" shine.

Material ReCreateLC has fluorescence, color stability and radiopacity.
In order to simulate dental tissues, material is produced in a wide range of VITA shades and has three levels of opacity.

Universal light-curing restorative composite ReCreateLC is intended for use in aggressive biological medium at a temperature range from 32°C to 42°C (in oral cavity at the temperature of (37±1 )°C and humidity of 60-90 %).

INDICATIONS :

Restoration of all cavity classes according to Black
Core Build-ups
Splinting
Correction of composite restorations
Fabrication of indirect restorations (inlays, onlays, veneers).

CONTRAINDICATIONS :

Apply carefully to patients with allergy to methacrylates.

Time of curing and thickness of the layer is determined by transparency of material :

FEATURES:

Excellent polishing
Does not stick to instrument
Keeps stable at modeling
Excellent radiopacity
Fluorescence
High surface hardness
High pressure resistance
Higher filler content and lower polymerization shrinkage.
Superior handling and easy to apply

KEY SPECIFICATION:

Shades :

Universal shades - A1 A2 A3 A3.5 A4 B1 B2

Dentine-opaque shades (O) - OA2 OA3

Transparent shades - Incisal (clear) (TC)

COMPOSITION :

Dimethacrylate oligomers (TEGDMA, UDMA, bis-EMA)
Combined radiopaque filler from modified aluminosilicate glass (0.02-2.0 urn)
Nanosized particles of silicon oxide (5-20 nm)
The proportion of inorganic filler is approximately 80%

Physical Properties :

Compressive Strength MPa	390
Flexural Strength MPa	130
Flexural Modulus GPa	9.5
Diamtetral Tensile Strength MPa	65
Water Absorptiion μg/mm³	3.5
Solubility μg/mm³	0.17
Volumetric Shrinkage %	1.8
Radio-opacity mm Al	3.5